A methacrylic-acid production catalyst comprised of a heteropolyacid compound comprising phosphorous and molybdenum is regenerated by subjecting a mixture comprising the degraded catalyst, water, a nitrate radical, and an ammonium radical in a molar ratio relative to the nitrate radical of not higher than 1.3 to heat treatment at a temperature of 100°C or higher, subsequently drying the treated mixture to obtain a dried material, and calcining the dried material.例文帳に追加

劣化触媒と、水と、硝酸根と、硝酸根に対するモル比率が１．３以下のアンモニウム根とを含む混合物を１００℃以上で熱処理した後、乾燥して乾燥物を得、該乾燥物を焼成することにより、リン及びモリブデンを含むヘテロポリ酸化合物からなるメタクリル酸製造用触媒を再生する。 - 特許庁

In an electrolytic cell demarcated into an anode chamber and a cathode chamber by an electrolytic membrane, a radical hydrogen generated at a cathode in the cathode chamber by an electrolytic method is brought into contact with a nitrate nitrogen-containing wastewater in the presence of a catalyst separated from electrodes to reduce nitrate nitrogen to nitrogen.例文帳に追加

電解膜により陽極室と陰極室に区画された電解槽において、陰極室内で電解法により陰極で発生するラジカル水素と硝酸態窒素含有廃水とを電極から分離された触媒の存在下で接触させることにより、硝酸態窒素を窒素に還元処理する。 - 特許庁

The methacrylic-acid production catalyst comprised of a heteropolyacid compound comprising phosphorous and molybdenum, is regenerated by heat-treating the degraded catalyst at a temperature of 350°C or higher, subsequently mixing it with water, a nitrate radical, and an ammonium radical, thereafter drying the mixture to obtain a dried material, and calcining the dried material.例文帳に追加

劣化触媒を３５０℃以上で熱処理した後、水、硝酸根及びアンモニウム根と混合し、次いで乾燥して乾燥物を得、該乾燥物を焼成することにより、リン及びモリブデンを含むヘテロポリ酸化合物からなるメタクリル酸製造用触媒を再生する。 - 特許庁

This method for producing the spindle-shaped calcium carbonate having the small particle diameter comprises carrying out a carbonating reaction in a calcium hydroxide suspension containing one or more kinds of metal compounds selected from iron, manganese, copper, barium and strontium or a compound having nitrate radical added thereto.例文帳に追加

炭酸化反応を鉄、マンガン、銅、バリウム、ストロンチウムのなかから選ばれる１種以上の金属化合物、又は硝酸根を持つ化合物が添加されている水酸化カルシウム懸濁液中で行うことにより小粒子径の紡錐状炭酸カルシウムを製造する。 - 特許庁

The alcohol can be oxidized by a process in which a primary or secondary alcohol is reacted with an oxygen-containing gas in the presence of a catalyst composition containing (i) a stable free nitroxyl radical derivative, (ii) a nitrate source, (iii) a bromide source, and (iiii) a carboxylic acid, thereby obtaining an aldehyde or a ketone.例文帳に追加

アルコールは、（ｉ）安定なニトロキシルフリーラジカル誘導体、（ｉｉ）硝酸塩源、（ｉｉｉ）臭化物源及び（ｉｉｉｉ）カルボン酸を含有する触媒組成物の存在で第一アルコール又は第二アルコールを酸素含有ガスと反応させる方法によって酸化されることができ、それによりアルデヒド又はケトンが得られる。 - 特許庁